S235JR Galvanized pipe
235MPa. This material can be formed into many products such as I beams,channels, plates, angle bars etc.its excellent weldability makes it to be widely used in bridges,transmission towers etc.
235MPa. This material can be formed into many products such as I beams,channels, plates, angle bars etc.its excellent weldability makes it to be widely used in bridges,transmission towers etc.
235MPa. This material can be formed into many products such as I beams,channels, plates, angle bars etc.its excellent weldability makes it to be widely used in bridges,transmission towers etc. It is equivalent to Fe360B. Any steel with similar chemical and mechanical properties can be designated as S235JR material.
S235JR Galvanized pipe Parameter
| Standard | ASTM A53, BS1387-85, GB/T3091-08, DIN2440, JIS-G3444, EN10240, EN10255 etc. |
| Grade | Q195, Q215, Q235, Q345, S235JR, S275JR, STK400, STK500 etc. |
| Type & Zinc Coating | Hot dip galvanized steel pipe (zinc coating: 60g/m2-275g/m2) |
| Pre-painted galvanized steel pipe (zinc coating: 80g/m2-275g/m2) | |
| Outer Diameter | Round pipe: 17mm-273mm |
| Square pipe: 15mm x 15mm - 400mm x 400mm | |
| Rectangular pipe: 10mm x 20mm -200mm x 400mm | |
| Wall Thickness | Round pipe: 0.6mm-12mm |
| Square pipe: 0.6mm-20mm | |
| Rectangular pipe: 0.6mm-20mm | |
| Length | Length: 2m-5.8m/6m/12m ( We can adjust length according to your request) |
| Process | Cold Drawn Tube / Hot Rolled Tube |
| Testing Methods | Pressure test, Flaw detection, Eddy current testing, Hydrostatic testing or Ultrasonicexamination and also with chemical and physical property inspection |
| Third Party Inspection | SGS / BV / MTC etc. |
| Payment Terms | FOB 30%T/T,70% before shipment or CIF 30% pre-payment and the balance to be paid upon B/L (copy) |